Preparation And Characterization Of Resistant Wollastonite

Abstract

The objective of this study is to elaborated of the wollastonite (CaSiO3), prepared from silicon dioxide (SiO2) and calcium oxide (CaO) of the deposit d’El Khroub (Constantine), using synthesis by the solid method. the prepared samples were also characterized by X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy and the mechanical tests was performed The results shows that 1100 °C is the best sintering temepature, it has been found that the density is about 97 % of the theoretical density value of wollastonite, X-ray analysis reveals that the phase appears is only that of wollastonite. This result has been confirmed by Fourier transform infrared spectroscopy ===================================================================================================== L’objectif de cette étude est d'élaborer de la wollastonite (CaSiO3) à partir de dioxyde de silicium (SiO2) et d’Oxyde de Calcium (CaO) du gisement d’El Khroub (Constantine), en utilisant la synthèse par la méthode solide. Les échantillons sont caractérisés par diffraction des rayons X, la spectroscopie Infrarouge, microscopie électronique à balayage et les tests mécaniques ont été effectués Les résultats montrent que 1100 °C est la meilleure température de frittage et un taux de frittage égale 97 %la valeur de la densité théorique de wollastonite, l’analyse par diffraction des rayons X révèlent que la phase apparait est celui wollastonite. Ces résultats ont été confirmé par la spectroscopie Infrarouge.