| Titre: | Elaboration d'un composite sic-AL2O3 |
| Auteur(s): | Abdelhalek, brahimi |
| Mots-clés: | SiC-Al2O3, Kaolin DD3, PLPS |
| Date de publication: | 2-déc-2024 |
| Collection/Numéro: | Mémoire de Master; |
| Résumé: | The aim of this study is the elaboration of SiC-Al2O3 based composite, SiC-Al2O3 was successfully fabricated by pressureless liquid phase sintering in air at 1300 – 1500 °C. DD3 kaolin was used as a binder and sintering aid. The effect of sintering temperature on the mechanical performance and physical proprieties was systematically investigated. The results show for an open porosity of 28.36 % a sample with 5 % kaolin shows the strongest compression resistance of 197.17 MPa when sintered at 1500 °C and the strongest tensile resistance of 31.90 MPa when sintered at 1300 °C. |
| URI/URL: | http://dspace.univ-setif.dz:8888/jspui/handle/123456789/4763 |